A380 Aluminum Die Casting

A380 Aluminum Die Casting

Aluminum 384.0-f Die Casting Alloy Custom Manufacturering Product Description and Process Aluminum 384.0-f Die Casting Alloy Custom Manufacturering Production process: aluminum die casting process Machining process: CNC machine, machining center, lathe, mill machine, drill machine, etc. Surface...

Send Inquiry Chat Now

Aluminum 384.0-f Die Casting Alloy Custom Manufacturering

Product Description and Process

Aluminum 384.0-f Die Casting Alloy Custom Manufacturering

Production process: aluminum die casting process

Machining process: CNC machine, machining center, lathe, mill machine, drill machine, etc.

Surface treatment process: anodic oxidation, Dacromet coating, etc.


Product Material and Uses

Normally produce with JIS ADC1, ADC3, ADC5, ADC6, ADC10, ADC12, ASTM A413, A360, A380, A383, etc.

The aluminum casting products are widely used for electronic industry, auto-car parts, electric motor parts, aero craft parts, watercraft parts, medical treatment equipment, communication system, other machinery components, etc.  


MAGNESIUM ALLOYS

Magnesium alloys are noted for low weight, high strength to weight ratio, exceptional damping capacity and ease of machining. Magnesium die casting temperatures are about the same as aluminum and both hot chamber and cold chamber die casting machines are used to produce castings.

Magnesium die casting rates are high because of its low heat content which produces rapid solidification. For the same reason, less energy is required to heat the metal to casting temperature.

AZ91HP (high purity) alloy has been developed for die casting parts subject to corrosive environments. Because of lower levels of nickel, iron, copper and silicon versus AZ91D, this alloy is finding applications in automobiles, computers and peripheral equipment and in other die casting products where paint or coatings are either undesirable or expensive.

Although magnesium die castings are used uncoated, they can be finished in a variety of ways to give increased protection against corrosion, wear and abrasion resistance and to improve appearance. Common inorganic treatments include chemical dips, anodizing and plating. Organic coatings — oil, wax, resin or paint — are usually applied over chemical treatments or anodizing to seal the surface.


COMPOSITION AND PROPERTIES OF MAGNESIUM ALLOY FOR DIE CASTING ALLOYS

DESIGNATION

ASTM

COMPOSITION percent unless shown as range

STANDARD ALLOY   AZ91D

HIGH PURITY   ALLOY AZ91HP

AM60B

Aluminum

8.3 to 9.7

85. to 9.5

5.5 to 6.5

Zinc

0.35 to 1.0

0.45 to 0.9

0.22 max

Manganese, min.

0.13

0.15

0.24-0.6

Silicon, max.

0.5

0.20

0.10 max

Copper, max

0.30

0.015

0.010 max

Iron

0.005

-

0.005

Nickel, max

0.03

0.001

0.002 max

Others, total, max.

0.3

0.01

0.02

Magnesium

Bal.

Bal.

Bal.

PROPERTIES (see notes)

---

DESIGNATIONS

STANDARD ALLOY   AZ91D

HIGH PURITY   ALLOY AZ91HP

AM60B

Ultimate tensile strength (ksi)

34

34

32

Yield Strength (0.2% offset) (ksi)

23

23

19

Elongation, (% in 2″ G.L.)

3

3

8

Hardness (HB)

-

-

-

Shear Strength (ksi)

20

20

N/A

Compressive Yield Strength, (ksi)

22

22

19

Ultimate Compressive Strength, (ksi)

58

58

Fatigue Strength, (ksi) (limit @ 500 million cycles)

14

14

Specific Gravity

1.80

1.80

Density (lb./in.3)

0.066

0.066

0.065

Melting range

875-1105oF

875-1105oF

1005-1140oF

Thermal conductivity, CGS

0.17

0.17

Thermal Expansion, in./in./oF (x10-6)

15.2

15.2

14.2

Electrical Conductivity, (% I.A.C.S.)

10

10